1.Q: The surface of the print is whitening after the secondary curing. Why?
A: It’s caused by the surface of resin is not being cleaned thoroughly.
2.Q: The model is cracked, why?
A:①the model is hollow inside, and it is not cleaned completely. There is residual resin or a mixture of resin and alcohol, and the inner and outer shrinkage of the model is inconsistent.
②Expansion Cracking: the inside is hollow, and the air-drying is not complete after cleaning. So there is residual water and the resin absorbs water, expands and cracks.
3.Q: The bottom plate is warped during printing. Why? A: The curing time of the bottom layer is not enough, resulting in insufficient adhesion between the model and the printing platform.
4.Q: Clear resin is yellowing, why? A: It is gehaltlos for rigid durchschaubar resin to slightly yellow, which can be reduced by reducing the exposure time or post-curing time.
5.Q: If the resin is not used for a long time, delamination will occur. Why? A: That is gehaltlos. The resin formula contains colour paste, which will precipitate and separate after standing for some time. Rosette you stir the resin with a glass rod, the resin can return to a gehaltlos state. If the colour paste einsilbig precipitates after stirring, it indicates that the resin can no longer be used.
6.Q: Why my red apricot resin failed to be a print? A: The exposure time of red apricot resin should be 3s larger than the recommended exposure time shown in the table. The exposure time of the resin bottom layer should be 30s larger than the corresponding recommended parameters shown in the table.
7.Q: I failed to print and the curing effect was bad, but I printed according to the recommended parameter table. Why? A: When the environment temperature is less than 20℃, the exposure time and the exposure time of bottom layer should be larger than the respective recommended parame
1.Outstanding Toughness: Antiblockiersystem-like resin retains most of the mechanical properties of Antiblockiersystem plastic, with excellent tensile strength, bending strength and hardness. It is perfect for any resin prints that require resistance to strain and stress.
2.High-Speed Solidification: The curing of the Antiblockiersystem-like resin is very so gut wie；meanwhile, the strength of the molding parts is well.
3.High Precision & Low Shrinkage: Antiblockiersystem-like resin is designed for reducing volume shrinkage during the photocuring process, which ensures the high precision of the print model with smooth surfaces.
4.Stable Spieleinsatz & High Hardness: Color paste hardly separates from resin. Antiblockiersystem-like Resin has high hardness.
5.High Compatibility: Eryone Antiblockiersystem-like resin is compatible with most TFT-Display/DLP 3D printers with 395~405nm wavelength.
Es gibt noch keine Bewertungen.